Papua New Guinea 201 Stainless Steel Bar
Category:
Product Description
201 Stainless Steel Bar Description
201 stainless steel bar is composed primarily of iron with between 16 and 18% chromium and less than 0.15% carbon. It also contains small amounts of manganese, nickel, silicon, nitrogen, and copper. In addition, it can be hardened by cold working processes but not heat-treated like 304 or 316 grades, since it has higher formability than the 300 series grades. 201 stainless steel bar has high manganese but low nickel content. So its corrosion resistance is not as superior as 300 series. 201 stainless steel bars are widely used as parts in manufacturing kitchenware, outdoor decoration engineering, urban decoration industry and low-grade household products. They are also used in medical instruments and automotive parts that require flexibility while maintaining strength under pressure.
Product Parameters
|
Product Name |
201 Stainless Steel Bar |
|
|
Type |
Steel Bar |
|
|
Outer Diameter |
Round Bar |
4mm-500mm |
|
Hexagon Bar |
18mm-57mm (11/16″ to 2-3/4″) |
|
|
Square Bar |
18mm-47mm (11/16″ to 1-3/4″) |
|
|
Flat Steel |
1/2 "to 10", Thickness: 2mm-150mm, Can provide customized |
|
|
Length |
1-6 meters, Length can be customized |
|
|
Standard |
ASTM, AISI, JIS, GB, DIN, EN, etc. |
|
|
Surface |
Black, Bright Polished, Rough Turning, Mattness Surface Treatment, No. 4. BA, etc. |
|
|
Scope of Application |
Stainless steel bars are used in a variety of industries such as shipbuilding, Defense, Automotive, Textiles, Paper and pulp, Manufacturing, Cement, Heavy earthmoving equipment and construction, etc. |
|
Chemical Composition
|
C |
Si |
Mn |
Cr |
Ni |
S |
P |
|
≤ 0.15 |
≤ 0.75 |
5.50~7.50 |
16.00~18.00 |
3.50~5.50 |
≤ 0.03 |
≤ 0.06 |
Mechanical Properties
|
Tensile Strength Kb (MPa) |
Yield Strength σ0.2 (MPa) |
Elongation D5 (%) |
Hardness |
|
≥ 520 |
≥ 275 |
≥55-60 |
≤ 183HB；≤ 100 HRB |
Physical Performance
|
Density(g/cm³) |
Modulus of Elasticity(Gpa) |
Coefficient of Thermal Expansion(10-6/°C) |
Coefficient of Thermal Conductivity(W/m*K) |
Resistivity(μohm.in) |
|
7.8 |
197 |
15.7 |
16.2 |
27 |